▍ Product Advantage
1. Aluminum alloy with Mg as the main alloying element, the magnesium content is between 3-5%. Can also be called aluminum magnesium alloy.
2. Can not be strengthened by heat treatment
3. The density is small (5052 density is 2.68), and the weight of aluminum magnesium alloy is lower than that of other series under the same area.
4. The strength is higher than 1, 3 series, is a high-strength aluminum alloy, fatigue and welding performance is good. High tensile strength, high elongation.
5. Good corrosion resistance to Marine atmosphere.
6. It belongs to the hot-rolled aluminum plate series, so it can do anode oxidation deep processing.
 |  |  |
▍ Technical Parameters
Item | Aluminum Plate / Sheet |
Standard | GB/T3190-2008, GB/T3880-2006, ASTM B209, JIS H4000-2006 etc |
Grade | 5052, 5083, 5754, 5005, 5A05 etc. |
Temper | O-H112 |
Tolerance | ±1% |
Surface Treatment | Mirrored, Brushed, Anodizing etc. |
Processing Service | Cutting, Decoil etc |
Edge | Mill edge, Cut edge |
Thickness | 10-200mm |
Width | 10-2200mm |
▍ Product Uses
Various auto parts, sheet metal parts; Mechanical parts, automotive, aircraft fuel tanks, warships, submarines; Containers, etc. 5083 used for welding parts of ships, automobiles and aircraft.
5052: Marine and transportation material, railway carriages inner and outer cabinet, oil and chemical industry storage device, equipment and medical device panel etc.
5083: Tanker, oil storage tank, drilling platform, ship board, deck, bottom, welded parts and edge panel, railway carriages board, automotive and aircraft panel, cooling device and automotive molding etc.
5754: Tanker body, car body panel, marine facilities, pressure container, transportation etc.
▍ Chemical Performance
Grade | Temper | Thickness (mm) | Tensile Strength (Rm/Mpa) | Yield Strength (Rp0.2/Mpa) | Elongation(%) | |
A50mm | A | |||||
5052 | O H111 | >0.20~0.50 | 170-215 | 65 | 12 | - |
>0.50~1.50 | 14 | - | ||||
>1.50~3.00 | 16 | - | ||||
>3.00~6.00 | 18 | - | ||||
>6.00~12.50 | 165-215 | 19 | - | |||
>12.50~80.00 | - | 18 | ||||
H22 H32 | >0.20~0.50 | 210-260 | 130 | 5 | - | |
>0.50~1.50 | 6 | - | ||||
>1.50~3.00 | 7 | - | ||||
>3.00~6.00 | 10 | - | ||||
H24 H34 | >0.20~0.50 | 230-280 | 150 | 4 | - | |
>0.50~1.50 | 5 | - | ||||
>1.50~3.00 | 6 | - | ||||
>3.00~6.00 | 7 | - | ||||
H28 H38 | >0.20~0.50 | 270 | 210 | 3 | - | |
>0.50~1.50 | 3 | - | ||||
>1.50~3.00 | 4 | - | ||||
H112 | >6.00~12.50 | 190 | 80 | 7 | - | |
>12.50~40.00 | 170 | 70 | - | 10 | ||
>40.00~80.00 | 170 | 70 | - | 14 | ||
Grade | Temper | Thickness (mm) | Tensile Strength (Rm/Mpa) | Yield Strength (Rp0.2/Mpa) | Elongation(%) | |
A50mm | A | |||||
5083 | O H111 | >6.30~12.50 | 270-345 | 115 | 16 | - |
>12.50~50.00 | - | 15 | ||||
>50.00~80.00 | -- | 14 | ||||
>80.00~120.00 | 260 | 110 | 12 | |||
>120.00~200.00 | 255 | 105 | 12 | |||
H22 H32 | >0.20~0.50 | 305-380 | 215 | 5 | - | |
>0.50~1.50 | 6 | - | ||||
>1.50~3.00 | 7 | - | ||||
>3.00~6.00 | 8 | - | ||||
H24 H34 | >0.20~0.50 | 340-400 | 250 | 4 | - | |
>0.50~1.50 | 5 | - | ||||
>1.50~3.00 | 6 | - | ||||
>3.00~6.00 | 7 | - | ||||
H116 H321 | >1.50~3.00 | 305 | 215 | 8 | - | |
>3.00~6.00 | 10 | - | ||||
>6.00~12.50 | 12 | |||||
>12.50~40.00 | - | 10 | ||||
>40.00~80.00 | 285 | 200 | - | 10 | ||
H112 | >6.00~12.50 | 275 | 125 | 12 | ||
>12.50~40.00 | 275 | 125 | - | 10 | ||
>40.00~80.00 | 270 | 115 | - | 10 | ||
>40.00~120.00 | 260 | 110 | - | 10 | ||
▍ Product Advantage
1. Aluminum alloy with Mg as the main alloying element, the magnesium content is between 3-5%. Can also be called aluminum magnesium alloy.
2. Can not be strengthened by heat treatment
3. The density is small (5052 density is 2.68), and the weight of aluminum magnesium alloy is lower than that of other series under the same area.
4. The strength is higher than 1, 3 series, is a high-strength aluminum alloy, fatigue and welding performance is good. High tensile strength, high elongation.
5. Good corrosion resistance to Marine atmosphere.
6. It belongs to the hot-rolled aluminum plate series, so it can do anode oxidation deep processing.
| | |
▍ Technical Parameters
Item | Aluminum Plate / Sheet |
Standard | GB/T3190-2008, GB/T3880-2006, ASTM B209, JIS H4000-2006 etc |
Grade | 5052, 5083, 5754, 5005, 5A05 etc. |
Temper | O-H112 |
Tolerance | ±1% |
Surface Treatment | Mirrored, Brushed, Anodizing etc. |
Processing Service | Cutting, Decoil etc |
Edge | Mill edge, Cut edge |
Thickness | 10-200mm |
Width | 10-2200mm |
▍ Product Uses
Various auto parts, sheet metal parts; Mechanical parts, automotive, aircraft fuel tanks, warships, submarines; Containers, etc. 5083 used for welding parts of ships, automobiles and aircraft.
5052: Marine and transportation material, railway carriages inner and outer cabinet, oil and chemical industry storage device, equipment and medical device panel etc.
5083: Tanker, oil storage tank, drilling platform, ship board, deck, bottom, welded parts and edge panel, railway carriages board, automotive and aircraft panel, cooling device and automotive molding etc.
5754: Tanker body, car body panel, marine facilities, pressure container, transportation etc.
▍ Chemical Performance
Grade | Temper | Thickness (mm) | Tensile Strength (Rm/Mpa) | Yield Strength (Rp0.2/Mpa) | Elongation(%) | |
A50mm | A | |||||
5052 | O H111 | >0.20~0.50 | 170-215 | 65 | 12 | - |
>0.50~1.50 | 14 | - | ||||
>1.50~3.00 | 16 | - | ||||
>3.00~6.00 | 18 | - | ||||
>6.00~12.50 | 165-215 | 19 | - | |||
>12.50~80.00 | - | 18 | ||||
H22 H32 | >0.20~0.50 | 210-260 | 130 | 5 | - | |
>0.50~1.50 | 6 | - | ||||
>1.50~3.00 | 7 | - | ||||
>3.00~6.00 | 10 | - | ||||
H24 H34 | >0.20~0.50 | 230-280 | 150 | 4 | - | |
>0.50~1.50 | 5 | - | ||||
>1.50~3.00 | 6 | - | ||||
>3.00~6.00 | 7 | - | ||||
H28 H38 | >0.20~0.50 | 270 | 210 | 3 | - | |
>0.50~1.50 | 3 | - | ||||
>1.50~3.00 | 4 | - | ||||
H112 | >6.00~12.50 | 190 | 80 | 7 | - | |
>12.50~40.00 | 170 | 70 | - | 10 | ||
>40.00~80.00 | 170 | 70 | - | 14 | ||
Grade | Temper | Thickness (mm) | Tensile Strength (Rm/Mpa) | Yield Strength (Rp0.2/Mpa) | Elongation(%) | |
A50mm | A | |||||
5083 | O H111 | >6.30~12.50 | 270-345 | 115 | 16 | - |
>12.50~50.00 | - | 15 | ||||
>50.00~80.00 | -- | 14 | ||||
>80.00~120.00 | 260 | 110 | 12 | |||
>120.00~200.00 | 255 | 105 | 12 | |||
H22 H32 | >0.20~0.50 | 305-380 | 215 | 5 | - | |
>0.50~1.50 | 6 | - | ||||
>1.50~3.00 | 7 | - | ||||
>3.00~6.00 | 8 | - | ||||
H24 H34 | >0.20~0.50 | 340-400 | 250 | 4 | - | |
>0.50~1.50 | 5 | - | ||||
>1.50~3.00 | 6 | - | ||||
>3.00~6.00 | 7 | - | ||||
H116 H321 | >1.50~3.00 | 305 | 215 | 8 | - | |
>3.00~6.00 | 10 | - | ||||
>6.00~12.50 | 12 | |||||
>12.50~40.00 | - | 10 | ||||
>40.00~80.00 | 285 | 200 | - | 10 | ||
H112 | >6.00~12.50 | 275 | 125 | 12 | ||
>12.50~40.00 | 275 | 125 | - | 10 | ||
>40.00~80.00 | 270 | 115 | - | 10 | ||
>40.00~120.00 | 260 | 110 | - | 10 | ||