| Quantity: | |
|---|---|
Product Features
1. Aluminum alloys with Mn as the main alloying element cannot be strengthened by heat treatment.
2. It has good plasticity, good welding performance, slightly stronger corrosion resistance than the 1 series, and is a medium-strength aluminum alloy.
3. Annealing temperature: low temperature annealing 260-360 °C, high temperature annealing 370-490 °C.
Technical Parameters
Item | Aluminum Coil |
Standard | GB/T3190-2008,GB/T3880-2006,ASTM B209,JIS H4000-2006 etc |
Grade | 3003 |
Temper | O, H12, H14, H16, H18, H24, H32 |
Surface Treatment | Mill finish, Mirrored, Brushed, Sandblasted, Embossed, Color Coated etc. |
Technology | Hot rolled ( DC ), cold rolling ( CC ), cast |
Thickness | 0.15-2.0mm |
Width | 10-2000mm |
Tolerance | ±1% |
Application | Heat sinks, LCD backplanes, bottle caps, cans, oxidation, mobile phone battery cases |
Chemical Performance
Grade | Temper | Thickness (mm) | Tensile Strength (Rm/Mpa) | Yield Strength (Rp0.2/Mpa) | Elongation(%) | |
A50mm | A | |||||
3003 | O H111 | >0.20~0.50 | 95-135 | 35 | 15 | - |
>0.50~1.50 | 17 | - | ||||
>1.50~3.00 | 20 | - | ||||
>3.00~6.00 | 23 | - | ||||
>6.00~12.50 | 24 | - | ||||
>12.50~50.00 | - | 23 | ||||
3003 | H12 | >0.20~0.50 | 120-160 | 90 | 3 | - |
>0.50~1.50 | 4 | - | ||||
>1.50~3.00 | 5 | - | ||||
>3.00~6.00 | 6 | - | ||||
3003 | H22 | >0.20~0.50 | 120-160 | 80 | 6 | - |
>0.50~1.50 | 7 | - | ||||
>1.50~3.00 | 8 | - | ||||
>3.00~6.00 | 9 | - | ||||
3003 | H14 | >0.20~0.50 | 145-195 | 125 | 2 | - |
>0.50~1.50 | 2 | - | ||||
>1.50~3.00 | 3 | - | ||||
>3.00~6.00 | 4 | - | ||||
3003 | H24 | >0.20~0.50 | 145-195 | 115 | 4 | - |
>0.50~1.50 | 4 | - | ||||
>1.50~3.00 | 5 | - | ||||
>3.00~6.00 | 6 | - | ||||
3003 | H19 | >0.20~0.50 | 210 | 180 | 1 | - |
>0.50~1.50 | 2 | - | ||||
>1.50~3.00 | 2 | - | ||||
Product Features
1. Aluminum alloys with Mn as the main alloying element cannot be strengthened by heat treatment.
2. It has good plasticity, good welding performance, slightly stronger corrosion resistance than the 1 series, and is a medium-strength aluminum alloy.
3. Annealing temperature: low temperature annealing 260-360 °C, high temperature annealing 370-490 °C.
Technical Parameters
Item | Aluminum Coil |
Standard | GB/T3190-2008,GB/T3880-2006,ASTM B209,JIS H4000-2006 etc |
Grade | 3003 |
Temper | O, H12, H14, H16, H18, H24, H32 |
Surface Treatment | Mill finish, Mirrored, Brushed, Sandblasted, Embossed, Color Coated etc. |
Technology | Hot rolled ( DC ), cold rolling ( CC ), cast |
Thickness | 0.15-2.0mm |
Width | 10-2000mm |
Tolerance | ±1% |
Application | Heat sinks, LCD backplanes, bottle caps, cans, oxidation, mobile phone battery cases |
Chemical Performance
Grade | Temper | Thickness (mm) | Tensile Strength (Rm/Mpa) | Yield Strength (Rp0.2/Mpa) | Elongation(%) | |
A50mm | A | |||||
3003 | O H111 | >0.20~0.50 | 95-135 | 35 | 15 | - |
>0.50~1.50 | 17 | - | ||||
>1.50~3.00 | 20 | - | ||||
>3.00~6.00 | 23 | - | ||||
>6.00~12.50 | 24 | - | ||||
>12.50~50.00 | - | 23 | ||||
3003 | H12 | >0.20~0.50 | 120-160 | 90 | 3 | - |
>0.50~1.50 | 4 | - | ||||
>1.50~3.00 | 5 | - | ||||
>3.00~6.00 | 6 | - | ||||
3003 | H22 | >0.20~0.50 | 120-160 | 80 | 6 | - |
>0.50~1.50 | 7 | - | ||||
>1.50~3.00 | 8 | - | ||||
>3.00~6.00 | 9 | - | ||||
3003 | H14 | >0.20~0.50 | 145-195 | 125 | 2 | - |
>0.50~1.50 | 2 | - | ||||
>1.50~3.00 | 3 | - | ||||
>3.00~6.00 | 4 | - | ||||
3003 | H24 | >0.20~0.50 | 145-195 | 115 | 4 | - |
>0.50~1.50 | 4 | - | ||||
>1.50~3.00 | 5 | - | ||||
>3.00~6.00 | 6 | - | ||||
3003 | H19 | >0.20~0.50 | 210 | 180 | 1 | - |
>0.50~1.50 | 2 | - | ||||
>1.50~3.00 | 2 | - | ||||