6 Series Aluminum Sheets Aluminum Alloy For Heat Sinks 6061 6063 6082

The main alloying elements of the 6 series are magnesium and silicon, representing the grades 6061, 6063, 6082 and so on. It has medium strength, good corrosion resistance, weldability and oxidation effect.
The main tempers are T4, T6 and T651.
The internal stress of T6 is large, and the processing will be deformed, so T651 is more suitable for processing.

Availability:

Quantity:



Inquire Add to Basket

Model:
6 series
Brand:
HONESTY-AL

Product Description

▍ Product Advantage

1. Aluminum alloy with magnesium and silicon as the main alloying elements

2. Heat treatment for strengthening (T4, T6)

3. Moderate intensity

4. High corrosion resistance

5. Good welding performance

6.Good formability and manufacturability

▍ Product Uses

Mainly used in construction, ships, rail vehicles, electronics, electrical electronics, durable consumer goods and other fields.

Mechanical parts with high strength, weldability and corrosion resistance are required. All kinds of tubes and rods, profiles and decorative components, heat sinks, etc.

6061: Commonly used in aerospace, automotive, marine, construction, etc., known for its excellent strength and corrosion resistance.
6063: Commonly used in the construction and decoration industry, known for its good weldability and surface treatment performance.
6082: Commonly used in aerospace, automotive, machinery, etc., known for its high strength and corrosion resistance.

▍ Technical Parameters

Item	Aluminum Plate / Sheet
Standard	GB/T3190-2008, GB/T3880-2006, ASTM B209, JIS H4000-2006 etc
Grade	6061, 6063, 6082 etc.
Temper	T3, T4, T6, T651 etc.
Tolerance	±1%
Surface Treatment	Mirrored, Brushed, Anodizing etc.
Processing Service	Cutting, Decoil etc
Edge	Mill edge, Cut edge
Thickness	10-200mm
Width	10-2200mm

▍ Chemical Performance

rade	Temper	Thickness (mm)	Tensile Strength (R_m/Mpa)	Yield Strength (R_p0.2/MPa)	Elongation(%)
rade	Temper	Thickness (mm)	Tensile Strength (R_m/Mpa)	Yield Strength (R_p0.2/MPa)	A_50mm	A
6061	O	0.40~1.50	≤150	≤85	14	-
		＞1.50~3.00			16	-
		＞3.00~6.00			19	-
		＞6.00~12.50			16	-
		＞12.50~25.00			-	16
	T4	0.40~1.50			12	-
		＞1.50~3.00			14	-
		＞3.00~6.00			16	-
		＞6.00~12.50			18	-
		＞12.50~40.00			-	15
		＞40.00~80.00			-	14
	T6	0.40~1.50	290	240	6	-
		＞1.50~3.00			7	-
		＞3.00~6.00			10	-
		＞6.00~12.50			9	-
		＞12.50~40.00			-	8
		＞40.00~80.00			-	6
		＞80.00~100.00			-	5
	F	＞2.50~150.00	-

Grade	Temper	Thickness (mm)	Tensile Strength (R_m/Mpa)	Yield Strength (R_p0.2/MPa)	Elongation(%)
					A_50mm	A
6063	O	0.50~5.00	≤130	-	20	-
		＞5.00~12.50			15	-
		＞12.50~20.00			-	15
	T4	0.50~5.00	150	-	10	-
		＞5.00~10.00	130		10	-
	T6	0.50~5.00	240	190	8	-
		＞5.00~10.00	230	180	8	-

Grade	Temper	Thickness (mm)	Tensile Strength (R_m/Mpa)	Yield Strength (R_p0.2/MPa)	Elongation(%)
Grade	Temper	Thickness (mm)	Tensile Strength (R_m/Mpa)	Yield Strength (R_p0.2/MPa)	A_50mm	A
6082	O	0.40~1.50	≤150	≤85	14	-
		＞1.50~3.00			16	-
		＞3.00~6.00			18	-
		＞6.00~12.50			17	-
		＞12.50~25.00	≤155	-	-	16
	T4	0.40~1.50	205	110	12	-
		＞1.50~3.00			14	-
		＞3.00~6.00			15	-
		＞6.00~12.50			14	-
		＞12.50~40.00			-	13
		＞40.00~80.00			-	12
	T6	0.40~1.50	310	260	6	-
		＞1.50~3.00			7	-
		＞3.00~6.00			10	-
		＞6.00~12.50	300	255	9	-
	F	＞4.50~150.00	-