Aluminum Sheet 6061 6063 6082 Aluminum Alloy For Automobiles

The main alloying elements of the 6 series are magnesium and silicon, representing the grades are 6061, 6063, 6082 and so on. It has medium strength, good corrosion resistance, weldability and oxidation effect.
The main tempers are T4, T6 and T651.
The internal stress of T6 is large, and the processing will be deformed, so T651 is more suitable for processing.

Availability:

Quantity:



Inquire Add to Basket

Model:
6 series
Brand:
HONESTY-AL

Product Description

▍ Product Advantage

1. Aluminum alloy with magnesium and silicon as the main alloying elements.

2. Heat treatment for strengthening (T4, T6).

3. Moderate intensity.

4. High corrosion resistance.

5. Good welding performance.

6. Good formability and manufacturability.

▍ Product Uses

Mainly used in construction, ships, rail vehicles, electronics, electrical electronics, durable consumer goods and other fields.

Mechanical parts with high strength, weldability and corrosion resistance are required. All kinds of tubes and rods, profiles and decorative components, heat sinks, etc.

6061: Railway inside and outside parts, board and bed plate, electronics, electrical appliances, consumer durables etc.

6063: Industry molding etc.

6082: Highly stressed applications includes roofing construction, transportation and marine as well as mold etc.

▍ Technical Parameters

Item	Aluminum Sheet
Standard	GB/T3190-2008, GB/T3880-2006, ASTM B209, JIS H4000-2006 etc
Grade	6061, 6063, 6082 etc.
Temper	T3, T4, T6, T651 etc.
Tolerance	±1%
Surface Treatment	Mirrored, Brushed, Anodizing etc.
Processing Service	Cutting, Decoil etc
Edge	Mill edge, Cut edge
Thickness	0.15-10.0mm
Width	10-2200mm

▍ Chemical Performance

Grade	Temper	Thickness (mm)	Tensile Strength (R_m/Mpa)	Yield Strength (R_p0.2/MPa)	Elongation(%)
Grade	Temper	Thickness (mm)	Tensile Strength (R_m/Mpa)	Yield Strength (R_p0.2/MPa)	A_50mm	A
6061	O	0.40~1.50	≤150	≤85	14	-
		＞1.50~3.00			16	-
		＞3.00~6.00			19	-
		＞6.00~12.50			16	-
		＞12.50~25.00			-	16
	T4	0.40~1.50			12	-
		＞1.50~3.00			14	-
		＞3.00~6.00			16	-
		＞6.00~12.50			18	-
		＞12.50~40.00			-	15
		＞40.00~80.00			-	14
	T6	0.40~1.50	290	240	6	-
		＞1.50~3.00			7	-
		＞3.00~6.00			10	-
		＞6.00~12.50			9	-
		＞12.50~40.00			-	8
		＞40.00~80.00			-	6
		＞80.00~100.00			-	5
	F	＞2.50~150.00	-

Grade	Temper	Thickness (mm)	Tensile Strength (R_m/Mpa)	Yield Strength (R_p0.2/MPa)	Elongation(%)
					A_50mm	A
6063	O	0.50~5.00	≤130	-	20	-
		＞5.00~12.50			15	-
		＞12.50~20.00			-	15
	T4	0.50~5.00	150	-	10	-
		＞5.00~10.00	130		10	-
	T6	0.50~5.00	240	190	8	-
		＞5.00~10.00	230	180	8	-

Grade	Temper	Thickness (mm)	Tensile Strength (R_m/Mpa)	Yield Strength (R_p0.2/MPa)	Elongation(%)
Grade	Temper	Thickness (mm)	Tensile Strength (R_m/Mpa)	Yield Strength (R_p0.2/MPa)	A_50mm	A
6082	O	0.40~1.50	≤150	≤85	14	-
		＞1.50~3.00			16	-
		＞3.00~6.00			18	-
		＞6.00~12.50			17	-
		＞12.50~25.00	≤155	-	-	16
	T4	0.40~1.50	205	110	12	-
		＞1.50~3.00			14	-
		＞3.00~6.00			15	-
		＞6.00~12.50			14	-
		＞12.50~40.00			-	13
		＞40.00~80.00			-	12
	T6	0.40~1.50	310	260	6	-
		＞1.50~3.00			7	-
		＞3.00~6.00			10	-
		＞6.00~12.50	300	255	9	-
	F	＞4.50~150.00	-